Flux-cored Wire (Iron-based, Cobalt-based)
Product Parameters
| 产品 牌号 | 产品化学成份（%） | 硬度(HRC) | 参照标准 | ||||||||
| Chemical Composition (%) | |||||||||||
| Product Name | C | Si | Mn | Mo | Cr | W | Ni | Fe | Co | Hardness | Reference Standard |
| CQCo-06 | 1.15 | 1.00 | ≤1.0 | ≤1.0 | 29.00 | 4.50 | ≤3.0 | ≤3.0 | Bal | 40-46 | AWS A5.21 ERCoCr-A |
| Stl. 6 | |||||||||||
| CQCo-12 | 1.40 | 1.20 | ≤1.0 | ≤1.0 | 29.00 | 8.00 | ≤3.0 | ≤3.0 | Bal | 44-50 | AWS A5.21 ERCoCr-B |
| Stl. 12 | |||||||||||
| CQCo-21 | 0.20 | 0.90 | ≤1.5 | 5.50 | 27.00 | 0.50 | 3.50 | ≤2.0 | Bal | 20-42 | AWS A5.21 ERCoCr-E |
| Stl. 21 | |||||||||||
Common wire models are listed below. Custom products are available for special hardfacing processes.
| 产品 牌号 | 产品化学成份（重量%） | 参照标准 | ||||||||
| Chemical Composition (Wt%) | ||||||||||
| Product Name | C | Cr | Ni | Mo | Mn | Si | P | S | Cu | Reference Standard |
| JHs8410 | 0.9 | 17.5 | 0.45 | 0.43 | 1 | 0.88 | 0.001 | 0.008 | 0.33 | AWS 5.22 E430T1-4 |
| SAMALLOY 430T1-4 | ||||||||||
| JHsR410 | 1 | 12 | 0.45 | 0.45 | 1.1 | 0.8 | 0.002 | 0.001 | 0.35 | AWS 5.22 E410T1-4 |
| SAMALLOY 410T1-4 | ||||||||||
| JHs309LMo | 0.01 | 23.5 | 14 | 2.6 | 1.75 | 0.7 | 0.005 | 0.004 | 0.3 | AWS 5.22 E309LMoT1-1 |
| SAMALLOY 309LMoT1-1 | ||||||||||
| JHs308L | 0.012 | 19 | 10 | 0.32 | 1.8 | 0.67 | 0.005 | 0.001 | 0.23 | AWS 5.22 E308LT1-1 |
| SAMALLOY 308LT1-1 | ||||||||||
| JHs316L | 0.011 | 18.7 | 12.9 | 2.3 | 1.9 | 0.5 | 0.006 | 0.002 | 0.33 | AWS 5.22 E316LT1-1 |
| SAMALLOY 316LT1-1 | ||||||||||
| JHs317L | 0.02 | 19.2 | 13.5 | 3.5 | 1.8 | 0.66 | 0.004 | 0.001 | 0.29 | AWS 5.22 E317LT1-1 |
| SAMALLOY 317LT1-1 | ||||||||||
Our tubular wires (2.0mm-4.0mm diameter, alloy content ≥50%) suit submerged arc, open arc and gas shielded welding. Ideal for wear, corrosion and high-temperature working conditions in metallurgy, mining, power and machinery industries.
Common submerged arc welding wire models are as follows：
| 产品名称 | 焊剂 | 硬度 | 化学成分（重量%）Chemical Composition(Wt%) | |||||||
| Product Name | HRC | C | Cr | Si | Mo | Mn | Fe | W | Ni | |
| JHS 103 | 107 | 54 | 5.15 | 27.50 | 1.50 | 4.50 | Bal | |||
| JHS 104 | 431 | 28 | 0.25 | 1.20 | 1.50 | 3.00 | Bal | |||
| JHS 224H | 107 | 53 | 0.55 | 6.50 | 0.65 | 1.10 | 1.80 | Bal | 1.50 | |
| JHS 414-S | 260 | 40 | 0.20 | 14.00 | 0.50 | 1.00 | 1.40 | Bal | 4.20 | |
| JHS 420 | 260 | 46 | 0.40 | 13.00 | 0.50 | 1.40 | Bal | |||
| JHS 423 | 107 | 45 | 0.33 | 13.50 | 0.50 | 1.20 | 1.50 | Bal | 2.50 | |
| JHS 424H | 260 | 49 | 0.40 | 12.00 | 0.50 | 0.90 | 2.20 | Bal | 1.40 | |
| JHS 430 | 260 | 0.10 | 19.00 | 0.50 | 0.70 | Bal | 0.60 | |||
| JHS 911 | 107 | 57 | 6.60 | 36.50 | 0.40 | 0.40 | Bal | |||
Common open arc welding wire models are as follows：
| 产品名称 | 硬度 | 化学成分（重量%）Chemical Composition(Wt%) | ||||||
| Product Name | HRC | C | Cr | Si | Mo | Mn | Fe | Ni |
| JHS 11-o | 50 | 3.20 | 14.50 | 0.90 | 0.45 | 1.40 | Bal | |
| JHS 94-o | 57 | 3.20 | 24.50 | 0.70 | 0.80 | Bal | 2.80 | |
| JHS 103-o | 58 | 5.5 | 27 | 0.9 | 1.90 | Bal | ||
| JHS 100HC-o | 60 | 5.50 | 26.50 | 2.40 | 1.30 | 1.90 | Bal | |
| JHS 117-o | 43 | 2.30 | 10.50 | 1.30 | 1.50 | 1.50 | Bal | |
| JHS 150-o | 58 | 2.20 | 7.00 | 2.00 | 1.00 | Bal | V:0.20 | |
| JHS 945-o | 57 | 5.00 | 21.50 | 0.70 | 4.50 | 0.70 | Bal | W:2.00 |
| JHS 94G | 52 | 3.00 | 28.00 | 1.40 | 1.20 | Bal | B:0.80 | |
| JHS 414N-o | 47 | 0.20 | 14.00 | 0.50 | 1.00 | 1.30 | Bal | 4.20 |
| JHS 103HD | 60 | 5.60 | 30.00 | 1.10 | 0.80 | 1.20 | Bal | |